High Purity 99.5% White Aluminum Oxide 0 - 1mm / 1 - 3mm

High Purity 99.5% White Aluminum Oxide 0 – 1mm / 1 – 3mm

/MT

High Purity 99.5% White Aluminum Oxide 0 – 1mm / 1 – 3mm

Wfa glass sandblasting white fused alumina stainless steel sandblasting. with the eye-catching white color and the advantage of high density and low micro porosity, it can effectively improve the volume stability and the thermal shock resistance of the material. It is the mainly raw material to produce middle or high level unshaped or shaped refractory material. It is applied to the unshaped refractory materials, such as refractory carstables for ladles, middle or high level iron runner casting material, gunning refractory and fabricate parts ect. It also can be used to kinds of corundum products, such as corundum bricks, corundum, mullite corundum, refining corundum perforated bricks, overall blowtorch and combined nozzle, side ceiling of the high temperature kiln, ect. All in all, it is widely used in steel, cement, ceramics, grinding material and petrochemical industries.

Aluminum oxide is used successfully for cleaning, deburring, surface finishing, rust removal and old paint coatings, preparing surfaces for subsequent anti-corrosion treatments with paint and primer at the highest quality standards.

PurposeSpecificationChemical Composition(%)Magnetic material content(%)max
Abrasives gradeAl2O3minFe2O3maxSiO2maxTiO2max
grain12-80#990.050.260.080.0023
90-150#990.060.280.090.0021
180-220#990.080.300.100.0018
micropowder240-10000#98.50.10.400.15
Refractory gradeGroup Size0-1mm
1-3mm
3-5mm
5-8mm
990.10.350.3
Fine Powder-100mesh
-200mesh
-350mesh
990.10.350.3
colorwhite
Hardness(mohs)9.0
Melting point(°C)2250
Maximum service temperature(°C)1900
Ture density(g/cm3)3.9

 

Reviews

There are no reviews yet.

Be the first to review “High Purity 99.5% White Aluminum Oxide 0 – 1mm / 1 – 3mm”

Your email address will not be published. Required fields are marked *

PDF-LOGO-100-.png

TDS not uploaded

PDF-LOGO-100-.png

MSDS not uploaded

Please enter correct URL of your document.

Scroll to Top