600# 800# 1000# white aluminum oxide lapping powder

White aluminum oxide is made by smelting and cooling above 2000 degrees in arc, grinding and shaping, removing iron by magnetic separation, and sieving into many kinds of granularity. It is compact in texture, high in hardness and sharp in shape.

$0.80$1.50 / MT

600# 800# 1000# white aluminum oxide lapping powder

white alumina oxide (2).jpg

Physical & Chemical

White Fused Alumina/ White Corundum/ White Aluminium Oxide in abrasive

Test items

indicators

Mohs hardness

9.0

Bulk density

1.75-1.95g/cm3

Real density

3.95g/cm3

Melting point

2250℃

The highest operating temperature

1900℃

Used for abrasive, lapping, polishing

Properties

Type

FEPA

F230 F240 F280 F320 F360 F400 F500 F600 F800

 F1000 F1200 F1500 F2000

JIS

240# 280# 320# 360# 400# 500# 600# 700# 800# 1000# 1200# 1500# 2000# 2500# 3000# 4000# 6000# 8000#

Guarantee Value

Typical Value

Chemical composition

AI2O3

99.0 min

99.2

SiO2

0.4 max

0.08

Fe2O3

0.2 max

0.06

Na2O

0.4max

0.35

Application

 1. white fused alumina Used for free grinding, such as glass industry.

2.white fused alumina  Used for friction products and wear-resistant floors.

3. white fused alumina Suitable for resin or ceramic bond abrasive, such as grinding wheel, cutting off grinding wheel,etc

4. white fused alumina Suitable for refractory, wear-resisting and refractory products.

5. white fused alumina Used for polishing, such as grindstone, grinding block, plate turning, etc.

6. white fused alumina Used for coating abrasive tools, such as sandpaper, emery cloth, sand belt, etc.

7. white fused alumina Used for precision casting, grinding, grinding, polishing mold production.

WHITE fused alumina (9).jpg

Packaging & Shipping

 -1.jpg

Reviews

There are no reviews yet.

Be the first to review “600# 800# 1000# white aluminum oxide lapping powder”

Your email address will not be published. Required fields are marked *

PDF-LOGO-100-.png

TDS not uploaded

PDF-LOGO-100-.png

MSDS not uploaded

Please enter correct URL of your document.

Scroll to Top